量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
The simultaneous control of the number and position of negatively charged nitrogen-vacancy (NV) centers in diamond was achieved. While single near-surface NV centers are known to exhibit outstanding capabilities in external spin sensing, trade-off relationships among the accuracy of the number and position, and the coherence of NV centers have made the use of such engineered NV centers difficult. Namely, low-energy nitrogen implantation with lithographic techniques enables the nanoscale position control but results in degradation of the creation yield and the coherence property. In this paper, we show that low-energy nitrogen ion implantation to a 12C (99.95%)-enriched homoepitaxial diamond layer using nanomask is applicable to create shallow NV centers with a sufficiently long coherence time for external spin sensing, at a high creation yield. Furthermore, the NV centers were arranged in a regular array so that 40% lattice sites contain single NV centers. The XY8-k measurements using the individual NV centers reveal that the created NV centers have depths from 2 to 12 nm, which is comparable to the stopping range of nitrogen ions implanted at 2.5 keV. We show that the position-controlled NV centers are capable of external spin sensing with a ultra-high spatial resolution.
Lithographically engineered shallow nitrogen-vacancy centers in diamond for external nuclear spin sensing