Microstructure of fatigue-tested F82H steel under multi-axial loadings
https://repo.qst.go.jp/records/49095
https://repo.qst.go.jp/records/49095156cda09-995b-48be-bb89-ce3059165b3d
| Item type | 学術雑誌論文 / Journal Article(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2018-07-04 | |||||
| タイトル | ||||||
| タイトル | Microstructure of fatigue-tested F82H steel under multi-axial loadings | |||||
| 言語 | ||||||
| 言語 | eng | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | journal article | |||||
| アクセス権 | ||||||
| アクセス権 | metadata only access | |||||
| アクセス権URI | http://purl.org/coar/access_right/c_14cb | |||||
| 著者 |
Fukumoto, K.
× Fukumoto, K.× Onitsuka, T.× Itoh, T.× 酒瀬川, 英雄× 谷川, 博康× Sakasegawa, Hideo× Tanigawa, Hiroyasu |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | The fatigue process of multi-axial low cycle fatigue in F82H steels was investigated via multi-axial fatigue tests under non-proportional loading at 573 K in air. Various strain paths and strain waveforms were employed and the microstructure of each fatigue-tested F82H steel was examined. Sudden cyclic softening occurred at the initial stage of 50 cycles and the failure life associated with the circle loading test was significantly lower than those corresponding to push–pull and reversed torsion loading tests. Dislocation formation increased rapidly under all loading conditions. At failure, the dislocation density generated by circle loading at Δεeq = 1.0% was tens of times larger than those of the other loadings. Sudden cyclic softening results from the formation of mobile dislocations in grain interiors during the initial stage of loading. The significant reduction in the lifetime is directly correlated with the high density of dislocations generated during circle loadings. |
|||||
| 書誌情報 |
Nuclear Materials and Energy 巻 15, p. 180-184, 発行日 2018-04 |
|||||
| 出版者 | ||||||
| 出版者 | Elsevier | |||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 2352-1791 | |||||
| DOI | ||||||
| 識別子タイプ | DOI | |||||
| 関連識別子 | 10.1016/j.nme.2018.04.008 | |||||
| 関連サイト | ||||||
| 識別子タイプ | DOI | |||||
| 関連識別子 | https://doi.org/10.1016/j.nme.2018.04.008 | |||||