@article{oai:repo.qst.go.jp:00082604,
 author = {Ishikawa, Norito and Tomitsugu, Taguchi and Ogawa, Hiroaki and Tomitsugu, Taguchi},
 issue = {4},
 journal = {Quantum Beam Science},
 month = {Dec},
 note = {Amorphizable ceramics (LiNbO3, ZrSiO4, and Gd3Ga5O12) were irradiated with 200 MeV Au ions at an oblique incidence angle, and the as-irradiated samples were observed by transmission electron microscopy (TEM). Ion tracks in amorphizable ceramics are confirmed to be homogenous along the ion paths. Magnified TEM images show the formation of bell-shaped hillocks. The ion track diameter and hillock diameter are similar for all the amorphizable ceramics, while there is a tendency for the hillocks to be slightly bigger than the ion tracks. For SrTiO3 (STO) and 0.5 wt% niobium-doped STO (Nb-STO), whose hillock formation has not been fully explored, 200 MeV Au ion irradiation and TEM observation were also performed. The ion track diameters in these materials are found to be markedly smaller than the hillock diameters. The ion tracks in these materials exhibit inhomogeneity, which is similar to that reported for non-amorphizable ceramics. On the other hand, the hillocks appear to be amorphous, and the amorphous feature is in contrast to the crystalline feature of hillocks observed in non-amorphizable ceramics. No marked difference is recognized between the nanostructures in STO and those in Nb-STO. The material dependence of the nanostructure formation is explained in terms of the intricate recrystallization process.},
 pages = {43-1--43-14},
 title = {Comprehensive Understanding of Hillocks and Ion Tracks in Ceramics Irradiated with Swift Heavy Ions},
 volume = {4},
 year = {2020}
}