量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
The β-hydrogen-free imidazole monomer, 2-methyl-N-methyl-4(5)-vinylimidazole (2M4VIm), is synthesized to prepare anion exchange membranes (AEMs). The radiation-induced graft polymerization of 2M4VIm and styrene is performed in poly(ethylene-co-tetrafluoroethylene), followed by N-alkylation and ion exchange reactions to prepare 4-vinylimidazolium-containing AEM (2M4VIm/St-AEM). AEMs that have a 6/4 2M4VIm/St molar ratio and 1.7 mmol g−1 ion exchange capacity (IEC) result in 75 mS cm−1 conductivity and 60% water uptake at room temperature in water, demonstrating enhanced values compared to previously reported 2-methyl-N-vinylimidazolium-containing AEMs (2MNVIm/St-AEM) that have a similar comonomer ratio and IEC. The small-angle neutron scattering measurements of dry and swollen 2M4VIm/St-AEM reveal hydrophilic/hydrophobic two-phase separation, as observed for 2MNVIm/St-AEM with a similar Im/St composition. 2M4VIm/St-AEMs exhibit higher alkaline stability in 1 m KOH at 80 °C at an early stage owing to the suppression of imidazolium β-elimination but lower long-term stability than that of 2MNVIm/St-AEM due to the ring-opening reaction of the imidazolium group due to its outward orientation from the graft main chain.
Synthesis and Characterization of 4-Vinylimidazolium/Styrene-Cografted Anion-Conducting Electrolyte Membranes