量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
The mechanical properties of reduced activation ferritic/martensitic steels (RAFMs) such as creep, thermal aging, and irradiation resistance are improved by the formation of MX and M23C6 particles. However, it is well known that these particles are unstable under irradiation. The purpose of the present study is to clarify the details of the radiation-induced amorphization (RIA) of M23C6 in F82H steels. The instability behavior of M23C6 under a wide range of irradiation temperatures from R.T. to 773 K and various ion beam energies (2.8, 3.7, 6.4 and 10.5 MeV) was systematically investigated. Two types of materials, F82H and its model alloy (F8), were utilized in this study. TEM observation and selected area electron diffraction analysis before and after irradiation were conducted to evaluate the occurrence of RIA, and the chemical composition was analyzed to reveal the possible relation between atom displacement/diffusion and RIA. In the case of the iron irradiation at the temperature below 598 K, a bilayer contrast of the particle, consisting of an amorphous-rim phase and inner crystalline core, was observed. Similar particle survived in the irradiated F82H at the temperature of 623 K, the RIA was not observed in the F8 specimen. Consequently, the critical temperature of RIA was estimated as 623–673 K. Since the melting temperature (Tm) of M23C6 is approximately 2173 K, the critical temperature corresponds to ∼0.29 Tm. From the STEM-EDS analysis, the Fe/Cr ratio of the particle decreased with increasing irradiation temperature in the range of 573–623 K. This behavior was qualitatively explained by the formation of the amorphous phase. It is clarified that the occurrence of the RIA of M23C6 particle can be evaluated by the variation of Fe/Cr ratio.
Study of radiation-induced amorphization of M23C6 in RAFM steels under iron irradiations