量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
The change in the positron annihilation lifetime (PAL) of vacancy clusters before and after electrolysis hydrogen charging was determined using PAL measurements in electron-irradiated F82H. The experimental change indicated 8 hydrogen atoms were trapped in vacancy clusters; whereas the theoretical calculation resulted in approximately 14 atoms. As the samples were left at room temperature for 5 min until the start of the PAL measurements, the de-trapping effect of hydrogen atoms was also considered; approximately 13 hydrogen atoms were captured at each vacancy cluster. The PAL decreased after annealing at 148 K, which could not be explained theoretically. Therefore, further experiments and discussions are needed to obtain a precise change in the PAL of vacancy clusters containing hydrogen atoms in F82H.
Change in the Positron Annihilation Lifetime of Vacancy Clusters Containing Hydrogen Atoms in Electron-Irradiated F82H