量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum and Radiological Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
Insulator-to-metal transition in Ca2RuO4 has drawn keen attention because of its sensitivity to various stimulation and its potential controllability. Here, we report a direct observation of Fermi surface, which emerges upon introducing excess oxygen into an insulating Ca2RuO4, by using angle-resolved photoemission spectroscopy. Comparison between energy distribution curves shows that the Mott insulating gap is closed by eV-scale spectral-weight transfer with excess oxygen. Momentum-space mapping exhibits two square-shaped sheets of the Fermi surface. One is a hole-like ???? sheet around the corner of a tetragonal Brillouin zone, and the other is an electron-like ???? sheet around the Γ point. The electron occupancies of the ???? and ???? bands are determined to be ???????? = 1.6 and ???????? = 0.6, respectively. Our result indicates that the insulator-to-metal transition occurs selectively in ???????????? and ???????????? bands and not yet in ???????????? band. This orbital selectivity is most likely explained in terms of the energy level of ????????????, which is deeper for Ca2RuO4+???? than for Ca1.8Sr0.2RuO4. Consequently, we found substantial differences from the Fermi surface of other ruthenates, shedding light on a unique role of excess oxygen among the metallization methods of Ca2RuO4.
Emergence of low-energy electronic states in oxygen-controlled Mott insulator Ca2RuO4+δ