量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
Reduced activation ferritic/martensitic (RAFM) steels are promising candidate for structural material of tritium breeding blanket in a fusion reactor. Database accumulation and definition of design criteria for RAFM have been intensively studied together with the progress of blanket design activities. As a part of database accumulation for fusion blanket, a RAFM steel, F82H was fatigue-tested at 573 and 673 K in the air. Axial strain-controlled fatigue tests were carried out with a cylindrical specimen with 8 mm of diameter with -1 of strain ratio condition in accordance with Japanese Industrial Standard, JIS Z 2279, “Method of high-temperature low cycle fatigue testing for metallic materials.” For high cycle tests, the maximum test cycles exceeded 10^6 cycles. Fatigue lifetime of F82H at temperatures ranging from room temperature to 673 K fell into the factor of 2 of the empirical fitting curve for 673 K. It was studied using experimental results that fatigue-related design limit based on RCC-MRx, such as fatigue design curves, half-life cyclic curves, and related coefficients.
Evaluation of fatigue properties of reduced activation ferritic/martensitic steel, F82H for development of design criteria