量研学術機関リポジトリ「QST-Repository」は、国立研究開発法人 量子科学技術研究開発機構に所属する職員等が生み出した学術成果（学会誌発表論文、学会発表、研究開発報告書、特許等）を集積しインターネット上で広く公開するサービスです。 Welcome to QST-Repository where we accumulates and discloses the academic research results(Journal Publications, Conference presentation, Research and Development Report, Patent, etc.) of the members of National Institutes for Quantum and Radiological Science and Technology.
Thank you very much for using our website. On the 11th of March 2019, this site was moved from our own network server to the JAIRO Cloud network server. If you previously bookmarked this site, that bookmark will no longer work. We would be grateful if you could bookmark the website again. Thank you very much for your understanding and cooperation.
To understand the fuel retention mechanism, correlation of surface chemical states and hydrogen isotope retention behavior determined by XPS (X-ray photoelectron spectroscopy) and TDS (Thermal desorption spectroscopy), respectively, for JET ITER-Like Wall samples from operational period 2011-2012 were investigated. It was found that the deposition layer was formed on the upper part of the inner vertical divertor area. At the inner plasma strike point region, the original surface materials, W or Mo, were found, indicating to an erosion-dominated region, but deposition of impurities was also found. Higher heat load would induce the formation of metal carbide. At the outer horizontal divertor tile, mixed material layer was formed with iron as an impurity. TDS showed the H and D desorption behavior and the major D desorption temperature for the upper part of the inner vertical tile was located at 370 °C and 530 °C. At the strike point region, the D desorption temperature was clearly shifted toward higher release temperatures, indicating the stabilization of D trapping by higher heat load.
Correlation of surface chemical states with hydrogen isotope retention in divertor tiles of JET with ITER-Like Wall