{"_buckets": {"deposit": "04e5ac25-a36e-4509-a3b2-bddd7da20fd0"}, "_deposit": {"created_by": 1, "id": "48864", "owners": [1], "pid": {"revision_id": 0, "type": "depid", "value": "48864"}, "status": "published"}, "_oai": {"id": "oai:repo.qst.go.jp:00048864", "sets": ["1"]}, "author_link": ["492243", "492247", "492248", "492250", "492239", "492245", "492246", "492249", "492244", "492238", "492242", "492241", "492240"], "item_8_biblio_info_7": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2017-10", "bibliographicIssueDateType": "Issued"}, "bibliographicPageStart": "014029", "bibliographicVolumeNumber": "T170", "bibliographic_titles": [{"bibliographic_title": "Physica Scripta"}]}]}, "item_8_description_5": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "High heat flux tests have been performed on 0.4 mm thick W coatings produced by vacuum plasma spraying on carbon-fiber composites (CFCs) for the future actively cooled W-coated CFC divertor target in JT-60SA. The surface temperature of the W coating increased up to 2000 °C at 15 MW m−2 for 5 s. No severe morphological changes, for example, melting, cracking and delamination were observed although recrystallization and grain growth were found in the W coating. Cyclic loading at 15 MW m−2 for 3 s with 50 cycles and additional 50 cycles with longer pulse length of 4 s produced again no severe morphological changes. Heat transfer analysis of the W-coated CFC sample during the high heat flux test showed that thermal resistance between W coatings and CFCs was negligibly low. This analysis also showed that the surface temperature of the 1 mm thick W coating on the actively cooled CFC monoblock divertor target in JT-60SA will be higher than the recrystallization temperature, 1200 °C, at the steady state heat flux of 15 MW m−2. Therefore, a reduction of armor thickness of the future actively cooled W-coated CFC monoblock divertor target in JT-60SA could be necessary to decrease the surface temperature to less than the recrystallization temperature.", "subitem_description_type": "Abstract"}]}, "item_8_relation_14": {"attribute_name": "DOI", "attribute_value_mlt": [{"subitem_relation_type_id": {"subitem_relation_type_id_text": "10.1088/1402-4896/aa8c54/meta", "subitem_relation_type_select": "DOI"}}]}, "item_8_relation_17": {"attribute_name": "関連サイト", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "http://iopscience.iop.org/article/10.1088/1402-4896/aa8c54/pdf"}], "subitem_relation_type_id": {"subitem_relation_type_id_text": "http://iopscience.iop.org/article/10.1088/1402-4896/aa8c54/pdf", "subitem_relation_type_select": "URI"}}]}, "item_8_source_id_9": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "0031-8949", "subitem_source_identifier_type": "ISSN"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "metadata only access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_14cb"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "福本, 正勝"}], "nameIdentifiers": [{"nameIdentifier": "492238", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Henri, Greuner"}], "nameIdentifiers": [{"nameIdentifier": "492239", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Bernd, Boeswirth"}], "nameIdentifiers": [{"nameIdentifier": "492240", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Stefan, Elgeti"}], "nameIdentifiers": [{"nameIdentifier": "492241", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Hans, Maier"}], "nameIdentifiers": [{"nameIdentifier": "492242", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Rudolf, Neu"}], "nameIdentifiers": [{"nameIdentifier": "492243", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "仲野, 友英"}], "nameIdentifiers": [{"nameIdentifier": "492244", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "黒木, 信義"}], "nameIdentifiers": [{"nameIdentifier": "492245", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "能見, 健司"}], "nameIdentifiers": [{"nameIdentifier": "492246", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "高畠, 剛"}], "nameIdentifiers": [{"nameIdentifier": "492247", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "吉田, 直亮"}], "nameIdentifiers": [{"nameIdentifier": "492248", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "福本 正勝", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "492249", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "仲野 友英", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "492250", "nameIdentifierScheme": "WEKO"}]}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "High heat flux testing of mm-thick tungsten coatings on carbon-fiber composites for the JT-60SA tokamak", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "High heat flux testing of mm-thick tungsten coatings on carbon-fiber composites for the JT-60SA tokamak"}]}, "item_type_id": "8", "owner": "1", "path": ["1"], "permalink_uri": "https://repo.qst.go.jp/records/48864", "pubdate": {"attribute_name": "公開日", "attribute_value": "2018-05-08"}, "publish_date": "2018-05-08", "publish_status": "0", "recid": "48864", "relation": {}, "relation_version_is_last": true, "title": ["High heat flux testing of mm-thick tungsten coatings on carbon-fiber composites for the JT-60SA tokamak"], "weko_shared_id": -1}
High heat flux testing of mm-thick tungsten coatings on carbon-fiber composites for the JT-60SA tokamak
https://repo.qst.go.jp/records/48864
https://repo.qst.go.jp/records/48864d216bc55-1158-43d9-968c-8170e42fb39a
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2018-05-08 | |||||
タイトル | ||||||
タイトル | High heat flux testing of mm-thick tungsten coatings on carbon-fiber composites for the JT-60SA tokamak | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
資源タイプ | journal article | |||||
アクセス権 | ||||||
アクセス権 | metadata only access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_14cb | |||||
著者 |
福本, 正勝
× 福本, 正勝× Henri, Greuner× Bernd, Boeswirth× Stefan, Elgeti× Hans, Maier× Rudolf, Neu× 仲野, 友英× 黒木, 信義× 能見, 健司× 高畠, 剛× 吉田, 直亮× 福本 正勝× 仲野 友英 |
|||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | High heat flux tests have been performed on 0.4 mm thick W coatings produced by vacuum plasma spraying on carbon-fiber composites (CFCs) for the future actively cooled W-coated CFC divertor target in JT-60SA. The surface temperature of the W coating increased up to 2000 °C at 15 MW m−2 for 5 s. No severe morphological changes, for example, melting, cracking and delamination were observed although recrystallization and grain growth were found in the W coating. Cyclic loading at 15 MW m−2 for 3 s with 50 cycles and additional 50 cycles with longer pulse length of 4 s produced again no severe morphological changes. Heat transfer analysis of the W-coated CFC sample during the high heat flux test showed that thermal resistance between W coatings and CFCs was negligibly low. This analysis also showed that the surface temperature of the 1 mm thick W coating on the actively cooled CFC monoblock divertor target in JT-60SA will be higher than the recrystallization temperature, 1200 °C, at the steady state heat flux of 15 MW m−2. Therefore, a reduction of armor thickness of the future actively cooled W-coated CFC monoblock divertor target in JT-60SA could be necessary to decrease the surface temperature to less than the recrystallization temperature. | |||||
書誌情報 |
Physica Scripta 巻 T170, p. 014029, 発行日 2017-10 |
|||||
ISSN | ||||||
収録物識別子タイプ | ISSN | |||||
収録物識別子 | 0031-8949 | |||||
DOI | ||||||
識別子タイプ | DOI | |||||
関連識別子 | 10.1088/1402-4896/aa8c54/meta | |||||
関連サイト | ||||||
識別子タイプ | URI | |||||
関連識別子 | http://iopscience.iop.org/article/10.1088/1402-4896/aa8c54/pdf | |||||
関連名称 | http://iopscience.iop.org/article/10.1088/1402-4896/aa8c54/pdf |